Conversion Tables
Conversion Table Wire AWG to mm² / qmm
AWG |
A (mm²) |
metric (mm²) |
R (Ohm/Km) |
Rated Current (A) *1 |
14 |
2,08 |
2,5 |
8,55 |
14 |
16 |
1,31 |
1,5 |
13,60 |
11 |
18 |
0,82 |
1,0 |
21,63 |
8,3 |
20 |
0,52 |
0,75 |
34,39 |
6,1 |
22 |
0,33 |
0,34 |
54,66 |
4,6 |
24 |
0,20 |
0,25 |
86,95 |
3,7 |
26 |
0,13 |
0,14 |
138,26 |
|
28 |
0,08 |
0,09 |
219,87 |
|
30 |
0,05 |
|
349,16 |
|
All values are for reference and no specification.
*1 PVC-Isolator at 80°C
Conversion Table Inch to Millimeter
Inch |
metric |
Class |
Gold Flash |
< 0,127 µm |
|
5 u'' |
0,127 µm |
III |
10 u'' |
0,254 µm |
II |
15 u'' |
0,381 µm |
|
20 u'' |
0,508 µm |
|
30 u'' |
0,762 µm |
I |
Properties of plastic material
Material |
HDT/A *1 |
Melting Point |
Water retention *2 |
LCP2 |
340° C |
350° C |
0,005% |
PA46 |
295° C |
295° C |
5,8% |
PA6/6T |
310° C |
310° C |
4,5% |
PPA |
330° C |
330° C |
1,4% |
LCP1 |
335° C |
335° C |
0,005% |
PPS |
320° C |
320° C |
0,02% |
PCT |
280° C |
280° C |
1,1% |
PBT |
225° C |
225° C |
0,3% |
*1 Heat Stability at1,82N/mm²
*2 According to ISO62